villatex В - ICOPAL
- category: ჰიდრო-რულონური
- Brands: ICOPAL
Roll-fed polymeric-bitumen SBS-modified material is made on a non-woven basis from high durability polyester with coarse-grained sand on the t... See more
Roll-fed polymeric-bitumen SBS-modified material is made on a non-woven basis from high durability polyester with coarse-grained sand on the top side. On the lower side the material has a longitudinally corrugated torchable layer developed by use of a protective “Profile SBS” technology and coated with an easily flammable polyethylene film.
See less
|
PARAMETER ITEM, MEASURE UNIT |
VALUE |
|
Width, m |
1 |
|
Length, m |
10 |
|
Weight, kg/m2 |
4,5 |
|
Base |
High durability polyester |
|
Breaking load under tension, N/50 mm, not lower |
650 |
|
Heat resistance during two hours at the temperature of °С, not lower |
90 |
|
Radius of curvature with radius at bent 25 mm at the temperature of °С, not above |
-15 |
|
Ductile-to-brittle transition temperature of polymeric-bitumen binder at the temperature of °С, not above |
-25 |
|
Waterproofing under a pressure 0.2 MPa during two hours, not less |
No signs of water leak |
|
Water absorption during 24 hours by weight, %, not above |
1,5 |
-
reliability and durability;
-
fast mounting;
-
applicable in all climatic zones of Russian Federation.
APPLICATION AREA
- Arrangement of new roofing and maintenance of old out-of-use roofing;
- Upper layer of a roofing system Villatex.
APPLICATION METHOD
- Fusion-bond to base.
Products offered
SINTAN Solo Vent FM ECM 6.5 kgm2 (17m)
- category: Waterproofing / Roll waterproofing
- Brands: ICOPAL
Aerator 100mm/290mm PG (set)
- category: Waterproofing / Roll waterproofing
- Brands: PROTECH GLOBAL
IMPER BALANCE (Т) Н 3,5 -TPP 3.5 kg / m2, 10 m2
- category: Roll waterproofing
- Brands: TECHNONICOL IMPER
Imper Standard (T) V - TKP 4.0 kg/m2, 10 m2
- category: Roll waterproofing
- Brands: TECHNONICOL IMPER
ANTIRADICE PE P 4mm F F 10m
- category: Waterproofing / Roll waterproofing
- Brands: POLYGLASS MAPEI GROUP
Imper Balance (T) B 4.5 - TKP 4.5 kg / m2, 10 m2
- category: Roll waterproofing
- Brands: TECHNONICOL IMPER
Plana P P 4.5 kg/sq.m (10 m) PLANA P 4.5 kg GRAY GF 10 m
- category: Waterproofing / Roll waterproofing
- Brands: POLYGLASS MAPEI GROUP
delivery
- When purchasing products for up to 100 GEL, the delivery price is 6 GEL;
- When purchasing products in the amount of 100 to 500 GEL, the delivery price is determined on the basis of: 1 km - 1.50 GEL;
- When purchasing products worth more than GEL 300, delivery is free (Tbilisi);
- The cost of delivery outside the city is determined at the rate: 1 km - 2 GEL.
Delivery time:
- Tbilisi | Rustavi | Mtskheta | Kutaisi | Batumi
Delivery time: 3-5 working days
- Out of town:
Delivery time: 4-5 working days
Note: Delivery is carried out only to the address, without unloading from the car and delivery to the apartment.
Product comparison
villatex В - ICOPAL
choose a product
- SINTAN Solo Vent FM ECM 6.5 kgm2 (17m)
- ICOpal Ultra В - ICOPAL
- Hydroizol TKP 3.2 (1*10m2)
- icopal ultra Н
- Vilatex in ECP 2.5 kg/sq.m (1*15m)
- Aerator 100mm/290mm PG (set)
- Hydroisol TPP 3.0 (1*10m2)
- Vilatex in ECP 4.0 kg/sq.m (1*10m)
- Vilatex in ECP 4.5 kg/sq.m (1*10m)
- IMPER STANDARD (X) 3kg/m2, 15m2
- IMPER BALANCE (Т) Н 3,5 -TPP 3.5 kg / m2, 10 m2
- Imper Standard (T) V - TKP 4.0 kg/m2, 10 m2
- ANTIRADICE PE P 4mm F F 10m
- Imper Balance (T) B 4.5 - TKP 4.5 kg / m2, 10 m2
- Plana P P 4.5 kg/sq.m (10 m) PLANA P 4.5 kg GRAY GF 10 m
|
PARAMETER ITEM, MEASURE UNIT |
VALUE |
|
Width, m |
1 |
|
Length, m |
10 |
|
Weight, kg/m2 |
4,5 |
|
Base |
High durability polyester |
|
Breaking load under tension, N/50 mm, not lower |
650 |
|
Heat resistance during two hours at the temperature of °С, not lower |
90 |
|
Radius of curvature with radius at bent 25 mm at the temperature of °С, not above |
-15 |
|
Ductile-to-brittle transition temperature of polymeric-bitumen binder at the temperature of °С, not above |
-25 |
|
Waterproofing under a pressure 0.2 MPa during two hours, not less |
No signs of water leak |
|
Water absorption during 24 hours by weight, %, not above |
1,5 |